1 Ph.D. Student, Department of Chemistry, Payame Noor University, Tehran, P.O. Box 19395-4697, Iran

2 Associate Professor, Department of Chemistry, Payame Noor University, Tehran, P.O. Box 19395-4697, Iran

3 Associate Professor, Abadan Faculty of petroleum Engineering, petroleum university of Technology, Abadan, Iran


In this paper, graphene oxide decorated with cerium oxide (CeO2) nanoparticles was prepared and used as anticorrosive pigments in epoxy nanocomposite coatings. The synthesized nanoparticle was characterized by FTIR, XRD, SEM, and EDX analyses. Graphene oxide decorated with CeO2 nanoparticles was dispersed in epoxy resin by sonication. The optimum nanoparticle content of the epoxy resin was studied by differential scanning calorimetry. The anticorrosive properties of these coatings were investigated using electrochemical impedance spectroscopy method and polarization in corrosive solution. Impedance parameters showed a decrease in the coating resistance over immersion time. The results indicated that the epoxy coatings containing nanoparticles could significantly increase the corrosion resistance of composite coatings compared to those of pure epoxy, and the highest value was obtained for 1% nanocomposite coatings after 270 days of immersion. Pull-off adhesion test showed that the highest value of adhesion was related to the coating containing 1% nanoparticles.


Main Subjects

Ain, Q.T., Haq, S.H., Alshammari, A., Al-Mutlaq, M.A., and Anjum, M.N., The Systemic Effect of PEG-nGO-Induced Oxidative Stress in Vivo in a Rodent Model, Beilstein Journal of Nanotechnology, Vol. 10, p. 901–911, 2019.
Bakhshandeh, E., Jannesari, A., Ranjbar, Z., Sobhani, S., and Saeb, M. R., Anticorrosion Hybrid Coatings Based on Epoxy-silica Nanocomposites: Toward Relationship between the Morphology and EIS Data, Progress in Organic Coatings, Vol. 77, p. 1169–1183, 2014.
Chang, C. H., Huang, T. C., Peng, C. W., Yeh, T. C., Lu, H. I., Hung, W. I., and Yeh, J. M., Novel Anticorrosion Coatings Prepared from Polyaniline/Graphene Composites, Carbon, Vol. 50, No. 14, p. 5044–5051, 2012.
Chelliah, M., Rayappan, J.B.R., and Krishnan, U.M., Synthesis and Characterization of Cerium Oxide Nanoparticles by Hydroxide Mediated Approach, Journal of Applied Sciences, Vol. 12, p. 1734–1737, 2012.
Chiong, S.J., Goh, P.S., and Ismail, A.F., Novel Hydrophobic PVDF/APTES–GO Nanocomposite for Natural Gas Pipelines Coating, Natural Gas Science and Engineering, Vol. 42, p. 190–202, 2017.
Di, H., Yu, Z., Ma, Y., Li, F., Lv, L., Pan, Y., and He, Y.., Graphene Oxide Decorated with Fe3O4 Nanoparticles with Advanced Anticorrosive Properties of Epoxy Coatings, Journal of the Taiwan Institute of Chemical Engineers, Vol. 64, p. 244–251, 2016.
Ebrahiminiya, A., Khorram, M., Hassanajili, S., and Javidi, M., Modeling and Optimization of the Parameters Affecting the In-situ Microencapsulation Process for Producing Epoxy-based Self-healing Anticorrosion Coatings, Particuology, Vol. 36, p. 59–69, 2018.
Ghanbari, A. and Attar, M. M., A Study on the Anticorrosion Performance of Epoxy Nanocomposite Coatings Containing Epoxy-silane Treated Nanosilica on Mild Steel Substrate, Journal of Industrial and Engineering Chemistry, Vol. 23, p. 145–153, 2015.
Huang, T. C., Su, Y. A., Yeh, T. C., Huang, H. Y., Wu, C. P., Huang, K. Y., and Wei, Y., Advanced Anticorrosive Coatings Prepared from Electroactive Epoxy-SiO2 Hybrid Nanocomposite Materials, Electrochimic Acta, Vol. 56, No. 17, p. 6142–6149, 2011.
Jiang, F., Zhao, W., Wu, Y., Dong, J., Zhou, K., Lu, G., and Pu, J., Anticorrosion Behaviors of Epoxy Composite Coatings Enhanced via Graphene Oxide with Different Aspect Ratios, Progress in Organic Coatings, Vol. 127, p. 70–79, 2019.
Kurth, D.G. and Bein, T., Thin Films of (3-Aminopropy1) Triethoxysilaneo No Aluminum Oxide and Gold Substrates, Langmuir, Vol. 11, p. 3061–3067, 1995.
Li, J., Ecco, L., Ahniyaz, A., and Pan, J., Probing Electrochemical Mechanism of Polyaniline and CeO2 Nanoparticles in Alkyd Coating with In-situ Electrochemical-AFM and IRAS, Progress in Organic Coatings, Vol. 132, p. 399–408, 2019.
Mahulikar, P. P., Jadhav, R. S., and Hundiwale, D. G., Performance of Polyaniline/TiO2 Nanocomposites in Epoxy for Corrosion Resistant Coatings, Iranian Polymer Journal, Vol. 20, No. 5, p. 367–376, 2011.
Omrani, A., Rostami, A., Ravari, F., and Ehsani, M., The Relationship Between Composition and Electrical Properties of Brass Covered by a Nanocomposite Coating of Glycerol Diglycidyl Ether: An EIS and DMTA Study, Progress in Organic Coatings, Vol. 76, No. 2–3, p. 360–366, 2013.
Pourhashem, S., Vaezi, M.R., Rashidi, A., and Bagherzadeh, M.R., Exploring Corrosion Protection Properties of Solvent based Epoxy-graphene Oxide Nanocomposite Coatings on Mild Steel, Corrosion Science, Vol. 115, p. 78–92, 2017.
Ravari, F., Omrani, A., Rostami, A. A., and Ehsani, M., Ageing Effects on Electrical, Morphological, and Mechanical Properties of a Low Viscosity Epoxy Nanocomposite, Polymer Degradation and Stability, Vol. 97, p. 929–935, 2012.
Salili, S.M., Ataie, A., Barati, M.R., and Sadighi, Z., Characterization of Mechano-thermally Synthesized Curie Temperature-adjusted La0.8Sr0.2MnO3 Nanoparticles Coated with (3-aminopropyl) Triethoxysilane, Materials Characterization, Vol. 106, p. 78–85, 2015.
Schem, M., Schmidt, T., Gerwann, J., Wittmar, M., and Zheludkevich, M. L., CeO2-filled Sol-gel Coatings for Corrosion Protection of AA2024-T3 Aluminum Alloy, Corrosion Science, Vol. 51, p. 2304–2315, 2008.
Seza, A., Jafarian, H., Hasheminiasari, M., and Aliofkhazraei, M., Effect of Duty Cycle on Corrosion Resistance and Mechanical Properties of Tertiary Al2O3/Y2O3/Graphene Pulsed Electrodeposited Ni-based Nano-composite, Procedia Materials Science., Vol. 11, p. 576–582, 2015.
Sun, W., Wang, L., Wu, T., Pan, Y., and Liu, G., Synthesis of Low-electrical-conductivity Graphene/Pernigraniline Composites and Their Application in Corrosion Protection, Carbon, Vol. 79, No. 1, p. 605–614, 2014.
Tamizhdurai, P., Sakthinathan, S., Chen, S.M., Shanthi, K., Sivasanker, S., and Sangeetha, P., Environmentally Friendly Synthesis of CeO2 Nanoparticles for the Catalytic Oxidation of Benzyl Alcohol to Benzaldehyde and Selective Detection of Nitrite, Scientific Reports, Vol. 7, p. 46372, 2017.
Ubaid, F., Radwan, A. B., Naeem, N., Shakoor, R. A., Ahmed, Z., Montemor, M. F., and Soliman, A., Multifunctional Self-healing Polymeric Nanocomposite Coatings for Corrosion Inhibition of Steel, Surface and Coatings Technology, Vol. 372, p. 121–133 2019.
Wang, W., Wang, H., Zhao, J., Wang, X., Xiong, C., Song, L., and Li, W., Self-healing Performance and Corrosion Resistance of Graphene Oxide–mesoporous Silicon Layer–nanosphere Structure Coating under Marine Alternating Hydrostatic Pressure, Chemical Engineering Journal, p. 792–804, 2019.
Ye, Y., Zhang, D., Liu, T., Liu, Z., Pu, J., Liu, W., and Wang, L., Superior Corrosion Resistance and Self-healable Epoxy Coating Pigmented with Silanized Trianiline-intercalated Graphene, Carbon, Vol. 142, p. 164–176, 2019.
Yu, Z., Di, H., Ma, Y., Lv, L., Pan, Y., Zhang, C., and He, Y., Fabrication of Graphene Oxide-alumina Hybrids to Reinforce the Anticorrosion Performance of Composite Epoxy Coatings, Applied Surface Science, Vol. 351, p. 986–996, 2015.
Zamanizadeh, H. R., Shishesaz, M. R., Danaee, I., and Zaarei, D., Investigation of the Corrosion Protection Behavior of Natural Montmorillonite Clay/Bitumen Nanocomposite Coatings, Progress in Organic Coatings, Vol. 78, p. 256–260, 2015.
Zhang, X., Ma, R., Du, A., Liu, Q., and Cao, X., Corrosion Resistance of Organic Coating Based on Polyhedral Oligomeric Silsesquioxane-functionalized Graphene Oxide, Applied Surface Science, Vol. 484, p. 814–824, 2019.
Zhong, F., He, Y., Wang, P., Chen, C., and Chen, J., Self-assembled Graphene Oxide-graphene Hybrids for Enhancing the Corrosion Resistance of Waterborne Epoxy Coating, Applied Surface Science, Vol. 488, p. 801–812, 2019.